1、Different diamond and carbon-based composite films and structures have been successfully synthesized through CVD processes.

2、To date, good control of the crystallinity, orientation and phase distribution of diamond/silicon carbide composite films has become possible.

3、Graphene/3C-SiC and graphene/diamond hybrid nanolaminates have been synthesized. HRTEM analysis reveals that the the preferential nucleation of graphene at the planar defects of 3C-SiC, leading to the “splitting” of the 3C-SiC layer.

4、Diamond networks with both vertically and horizontally interconnected pores, have been fabricated using a simple template-free approach. The porosities are tunable in a large range. It shows great potential in sensing and energy-storage applications.

个人简介

1960年11月出生，国际知名金刚石薄膜领域专家，海外高层次人才引进计划专家、教育部“长江学者”讲座教授、国家级特聘专家、德国锡根大学表面技术与材料工程研究所所长、C4级（德国最高级别）终身讲座教授，山东省科学院海洋仪器仪表研究所特聘专家。1991年博士毕业于德国亚琛工业大学，师从2007年诺贝尔物理学奖获得者德国著名科学家Peter Grünberg 教授，1998年获得德国国家博士并获教授资格。姜辛教授长期致力于薄膜生长设计与应用研究，获得多项创新性成果，在相关领域处于国际领先地位。首次实现了金刚石在硅表面的异质外延生长，被公认为金刚石研究领域的重大突破；利用高分辨电子显微技术首次揭示了金刚石与硅基体界面的原子结构，建立了原子扩散控制的金刚石硅表面形核模型，实现了金刚石硅表面的定向形核；首次采用布里渊散射(Brillouin Scattering)与纳米压痕技术(Nano Indentation)对非晶薄膜材料的弹性力学性能进行了系统研究，相关论文成为该领域的开创性经典文章；率先使用氧化锌透明导电薄膜替代ITO用于有机发光器件电极；首次实现混合相纳米晶金刚石/β-碳化硅复合薄膜的制备，为扩展金刚石薄膜的应用奠定了坚实基础；利用气相沉积及原位硼掺杂技术成功研制出国际第一台金刚石电子硬度计。在Science、Nat.Mater.、Chem. Soc. Rev.、Adv. Mater.、Adv. Energy Mater.、Nat. Comm.等期刊上发表论文400余篇，他引超过8000余次，特邀报告100余次，撰写特邀综述性论文13篇，撰写论著5本，获得欧美专利12项。